Product description:
High weather resistance PVDF modified material has the characteristics of excellent weather resistance, high temperature resistance, organic solvent resistance, acid and alkali resistance, and strong self-cleaning ability. It is mainly used in the field of outdoor weather resistance. It can be used to prepare photovoltaic protective films, outdoor building materials protective films, and high dielectrics. Capacitor film and heating tape with electrical constant.
Product technical data sheet:
Note: This table is the test result of the product prepared into the photovoltaic package protective film, for reference only.Test items | Testing method | Unit | Standard value | Test value | |
Conventional performance | Film thickness | ISO 1593 | μm | >22.5 | 23 |
Density | ISO 1183 | g/cm³ | >1.7 | 1.75 | |
Breakdown voltage | ASTM D149 (oil) | % | >2.0 | 6.1 | |
Shrinkage(150℃,30min)MD | ISO 11501 | % | <2.0 | 0.88 | |
Shrinkage(150℃,30min)TD | ISO 11501 | % | <2.0 | 1.12 | |
Tensile strength MD | ISO527-3 | Mpa | >30 | 41 | |
Tensile strength TD | ISO527-3 | Mpa | >26 | 29 | |
Elongation at break MD | ISO527-3 | % | >100 | 273 | |
Elongation at break TD | ISO527-3 | % | >200 | 452 | |
Aging performance | Tensile strength( MD PCT96h) | ASTM D-882 | Mpa | >30 | 44 |
Tensile strength( TD PCT96h) | ASTM D-882 | Mpa | >25 | 30 | |
Elongation at break( MD PCT96h) | ASTM D-882 | % | >100 | 205 | |
Elongation at break( TD PCT96h) | ASTM D-882 | % | >10 | 42 | |
Yellowing value( ∆b PCT96h) | ASTM D-882 | / | <2.0 | 0.56 | |
Tensile strength ( MD DH3000h) | GB/T 2423.3-2006 | Mpa | >30 | 41 | |
Tensile strength ( TD DH3000h) | GB/T 2423.3-2006 | Mpa | >26 | 29 | |
Elongation at break(MD DH3000h) | GB/T 2423.3-2006 | % | >100 | 188 | |
Elongation at break(TD DH3000h) | GB/T 2423.3-2006 | % | >10 | 27 | |
Yellowing value(∆b DH3000h) | GB/T 2423.3-2006 | / | <2.0 | 0.74 | |
Tensile strength ( MD TC600) | GB/T 31034-2014 | Mpa | >30 | 44 | |
Tensile strength (TD TC600) | GB/T 31034-2014 | Mpa | >26 | 30 | |
Elongation at break(MD TC600) | GB/T 31034-2014 | % | >100 | 175 | |
Elongation at break(TD TC600) | GB/T 31034-2014 | % | >20 | 32 | |
Yellowing value(∆b TC600h) | GB/T 31034-2014 | / | <2.0 | 0.67 | |
Tensile strength(MD UV300Kwh) | IEC 61216-2005 | Mpa | >30 | 40 | |
Tensile strength(TD UV300Kwh) | IEC 61216-2005 | Mpa | >26 | 28 | |
Elongation at break(MD UV300Kwh) | IEC 61216-2005 | % | >100 | 150 | |
Elongation at break(TD UV300Kwh) | IEC 61216-2005 | % | >10 | 14 | |
Yellowing value(∆b UV300Kwh) | IEC 61216-2005 | / | <2.0 | 0.77 |
Note: This table is the test result of the product prepared into the photovoltaic package protective film, for reference only.
Contact information:
Jiaxing Gaozheng New Material Technology Co., Ltd.
No. 1,Tongche Road, Xincang Town, Pinghu City, Zhejiang Province
Tel:+86-(0)-13761189865
E-mail: wangpengpolymer@126.com
www.gztech.top